30 世 界 橡 胶 工 业

表4 性能参数

2005

单位

磁粉-10用量磁粉-10用量磁粉-10用量门尼粘度,100 硫化与-t90邵尔A硬度邵尔A硬度(老化后)拉伸强度扯断伸长率拉伸强度(老化后)扯断伸长率(老化后)体积电阻率

份质量分数体积分数MLmin--MPa%MPa% cm

NR1-标准00064.23.6261.566.327.358325.84993.85E+05

NR1-31003611.2643.5868.973.217.945217.33968.90E+041.5910.3756480.04370.00701.53

NR1-22005319.471.93.7173.177.415.342614.83594.80E+041.8680.557040.06800.01281.84

NR1-13506629.170.73.6379.983.910.23748.12558.10E+042.2510.5254700.08900.01932.11

NR2-标准000.056.93.4259.557.331.261728.25393.50E+061.050-----

NR2-130067.230.063.53.3979.574.611.34209.93592.00E+062.2000.3262300.09370.02072.77

NR2-260080.446.097.43.1992.587.36.13415.42821.70E+042.8700.4765410.15030.04674.02

EPDM-标准00061.64.967.370.414.545514.53987.30E+041.1250.47----

EPDM-3100287.962.56.0270.873.21237312.13313.0E+041.4350.4254190.03830.00631.47

EPDM-22004313.8655.5471.373.99.43489.43034.50E+041.6380.4554070.06800.01101.85

EPDM-14006125.377.94.274.677.45.43285.52964.50E+042.1160.7152370.11630.02472.46

密度导热率矫顽磁力HC最大极化强度剩余磁力导磁率

g cm3W m K(A m)(T)(T)-

1.1130.26----

导电性聚合物被广泛用于必须防止静电释放(ESO)或电磁干扰的场合。

3.6 铁磁性

磁粉是一种铁磁性材料,这意味着它起着软磁铁的作用,这种材料在外磁场中会被磁化但不能成为永久磁铁。有关铁磁性和表征它的特殊试验方法的基本情况已在过去的文献中描述过。

图7示出了胶料的导磁率。用导磁率材料中的磁通量密度描述,该密度与真空状态下相同磁场中心密度相对应。导磁率与胶料中磁粉的体积分数含量成正比。胶料的导磁率范围为1.5~4,这说明胶料具有铁磁性(导磁率<1为抗磁性胶料,磁导率>10为永久磁性胶料)。

胶料的其他磁性参数列于表4中。磁性极化强度就像顽磁那样,随着胶料中磁粉体积分数含量的增加而直线上升。每组胶料矫顽磁力保持不变。

鉴于填充磁粉的胶料具有铁磁性,因此,它可用来制造可移动的,或通过外磁铁原位固定

的零部件或者用于胶料易于检测的场合。

图7 磁粉-10的体积分数含量与导磁率的关系曲线

3.7 微波硫化性能

图8示出了不同胶料的微波硫化曲线。由于Fe3O4具有高的介电性和磁性损耗角正切值,因此可作为微波吸收材料的理想选择对象。

胶料在大约120 下硫化,由于胶料内部开始发泡(即硫化开始),所以温度不会升得太高,如果温度在120 以上时,其温度显示值是不可靠的。

在约35s内,不含磁粉的NR-1标准胶料

(下转第61页)